Stepanova L. N., Chernova V. V., Miloserdova M. A.
ACOUSTIC EMISSION CONTROL OF THE PROCESS OF DESTRUCTION OF CARBON FIBER SAMPLES AND THE WING BOX UNDER SHOCK LOADS
(pp. 4-11)

Abstract. Investigations of three groups of samples from carbon fiber T 700 and the composite wing box of the aircraft were carried out. Samples with monolayers laying 0; 90; –45 were subjected to shock loads, which were applied at their center with a load in the form of a blunt tip weighing 0.53 kg. Loads were dumped from a height of 0,3; 0,5; 1 m per sample. Impact damage with an energy of 15 J was also applied to the upper surface of the carbon fiber wing box. Acoustic emission (AE) signals were recorded from the piezoelectric antenna sensors mounted on the wing samples and box both during the impact of the weight with the object under study and during rebounds. The locations where the shock load were applied were located and the parameters of the AE signals were analyzed. The influence of the type of monolayer laying on the process of cracking in the material of the samples arising at different energy of shock loads was determined.

Keywords: Keywords: acoustic emission, carbon fiber, break, monolayer, shock load, wing box.

+ - About the Authors Click to collapse

L. N. Stepanova (Federal State Unitary Enterprise “Siberian Aeronautical Research Institute named after S. A. Chaplygin”, Novosibirsk, Russia) E-mail: Данный адрес e-mail защищен от спам-ботов, Вам необходимо включить Javascript для его просмотра.
V. V. Chernova, M. A. Miloserdova (The Siberian Transport University (STU), Novosibirsk, Russia) E-mail: Данный адрес e-mail защищен от спам-ботов, Вам необходимо включить Javascript для его просмотра.

+ - References Click to collapse

1. Madaras E. (2001). Highlights of NASA’s role in developing state-of-the-art nondestructive evaluation for composites: NASA Document ID 20050050900. Presented at the American Helicopter Sosiety Hampton Roads Chapter Structure Specialist Meeting. Williamsburg.
2. Prosser W., Madaras E., Studor G. (2005). Acoustic emission detection of impact damage on space shuttle structures. Journal of Acoustic Emission, Vol. 23, pp. 37 – 46.
3. Aljets D. (2011). Acoustic emission source location in composite aircraft structures using modal analysis. University of Glamorgan. PhD Thesis.
4. Cardoni M., Giglio M. (2014). A low frequency lamb waves based structural health monitoring of an aero-nautical carbon fiber reinforced polymer composite. Journal of Acoustic Emission, Vol. 32, pp. 1 – 20.
5. Guillaud N., Froustey C., Dau F., Viot P. (2015). Impact response of thick composite plates under uniaxial tensile preloading. Composite Structures, Vol. 121, pp. 172 – 181. [in Russian language]
6. Lopresto V., Langella A., Papa I. (2016). Residual Strength evaluation after impact tests in extreme conditions on CFRP laminates. Procedia Engineering, Vol. 167, pp. 138 – 142.
7. Dattoma V., Giancane S. (2013). Evaluation of energy of fatigue damage into GFRC through digital image correlation and thermography. Composites Part B: Engineering, Vol. 47, pp. 283 – 289.
8. Stepanova L. N., Chernova V. V. (2017). Analysis of the structural coefficients of acoustic emission signals under static loading of CFRP specimens with impact damage. Kontrol'. Diagnostika, (6), pp. 34 – 41. [in Russian language] DOI: 10.14489/td.2017.06.pp.034-041
9. Stepanova L. N., Ramazanov I. S., Bataev V. A. et al. (2019). Analysis of the dependence of the parameters of acoustic emission signals on changes in the structure of CFRP during strength tests of samples. Konstruktsii iz kompozitsionnyh materialov, (2), pp. 58 – 65. [in Russian language]
10. Barsuk V. E., Ser'eznov A. N., Stepanova L. N. et al. (2019). Acoustic emission control of defects in the wing box of an aircraft made of carbon fiber in the process of static and shock loading. Polet, (5), pp. 17 – 24. [in Russian language]
11. Stepanova L. N., Chernova V. V. (2019). Acoustic emission control of the destruction process of CFRP specimens under static load, positive and negative temperatures. Kontrol'. Diagnostika, (6), pp. 34 – 41. [in Russian language] DOI: 10.14489/td.2019.06.pp.034-041
12. Stepanova L. N., Anohin G. G., Chernova V. V. (2016). Using the acoustic emission method in cyclic testing of CFRP specimens with different types of monolayer stacking. Kontrol'. Diagnostika, (2), pp. 67 – 74. [in Russian language] DOI: 10.14489/td.2016.02.pp.066-074
13. Stepanova L. N., Kabanov S. I., Chernova V. V. (2019). Acoustic emission method for determining structural defects of a CFRP specimen. Ru Patent No. 2704144. [in Russian language]
14. Stepanova L. N., Kabanov S. I., Ramazanov I. S., Chernova V. V. (2018). Method for acoustic emission control of defects in composite structures based on CFRP. Ru Patent No. 2674573. [in Russian language]

+ - Purchase digital version of a single article Click to collapse

This article is available in electronic format (PDF).

The cost of a single article is 350 rubles. (including VAT 18%). After you place an order within a few days, you will receive following documents to your specified e-mail: account on payment and receipt to pay in the bank.

After depositing your payment on our bank account we send you file of the article by e-mail.

To order articles please copy the article doi:

10.14489/td.2020.09.pp.004-011

and fill out the form